Título: | Morphologies of nanostructured TiO2 doped with F on Ti-6Al-4V alloy |
Autor: | Hernández-López, Juan Manuel; Conde del Campo, Ana ; Domingo, Concepción CSIC ORCID; Damborenea, Juan de CSIC ORCID ; Arenas, M. A. CSIC ORCID | Fecha de publicación: | 2011 | Editor: | Pergamon Press | Citación: | Electrochimica Acta 56: 2221- 2229 (2011) | Resumen: | The formation of nanotubes in sulphuric/hydrofluoric acid electrolyte at controlled voltage is investigated on Ti-6Al-4V alloy used for load-bearing prosthetic applications. The effects of anodizing time and voltage on film morphology, composition and microstructure are studied by scanning and transmission electron microscopy, Rutherford backscattering spectroscopy (RBS), and Raman spectroscopy. Fluorine content in the films was of a particular interest for enhancement of antibacterial properties of the surface. The efficiencies of film formation are determined as about 40% and 80% for anodizing at 20 V and 60 V respectively for shorter anodizing time and as about 1 and 5% for longer anodizing time. For 5 min of anodizing, higher voltage conditions results in a thicker barrier layer. At extended anodizing time a further disruption of the nanotubular morphology and formation of approximately 1.5 μm-thick nanoporous film is promoted. The films grown at 20 V contain from 4 at.% to 6 at.% of fluorine. RBS detects about 13 at.% of fluorine incorporated in the film formed at 60 V for 60 min, possibly associated with a greater film thickness. The oxide film material consists of amorphous titania matrix doped with V2O5 and Al2O3. © 2010 Elsevier Ltd. | URI: | http://hdl.handle.net/10261/74505 | DOI: | 10.1016/j.electacta.2010.11.069 | Identificadores: | doi: 10.1016/j.electacta.2010.11.069 issn: 0013-4686 |
Aparece en las colecciones: | (CENIM) Artículos (CFMAC-IEM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
51
checked on 05-may-2024
WEB OF SCIENCETM
Citations
49
checked on 23-feb-2024
Page view(s)
320
checked on 16-may-2024
Download(s)
109
checked on 16-may-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.