Título: | Microstructure and properties of pitch‐based carbon composites |
Autor: | Blanco Rodríguez, Clara CSIC ORCID ; Santamaría Ramírez, Ricardo CSIC ORCID ; Bermejo Mayoral, Jenaro; Bonhomme, J.; Menéndez López, Rosa María CSIC | Fecha de publicación: | 1999 | Editor: | Wiley-VCH | Citación: | Journal of Microscopy 196(2): 213-224 (1999) | Resumen: | Pitches prepared in the laboratory by thermal treatment and air‐blowing of a commercial coal‐tar pitch were used as matrix precursors of carbon composites using granular petroleum coke, foundry coke, amorphous graphite and anthracite. Pitches were characterized by standard procedures (elemental analysis, softening point, solubility tests and carbon yield) and light microscopy (mesophase content). Pitch pyrolysis behaviour was monitored by thermogravimetric analysis and from the optical texture of cokes. Pitch wettability to the different carbons, at different temperatures, was also studied. Experimental conditions selected for the preparation of composites were based on pitch composition and properties. The main microstructural features of composites were determined by light microscopy and scanning electron microscopy. Composite properties were described in terms of their density, porosity and compressive strength, and related to composite microstructure and the characteristics of the precursors. Thermal treatment and air‐blowing of pitch improved carbon composite structure and properties. The lowest porosities and best mechanical properties were observed in those composites obtained with the thermally treated pitches combined with foundry coke and anthracite. | Versión del editor: | https://doi.org/10.1046/j.1365-2818.1999.00622.x | URI: | http://hdl.handle.net/10261/223307 | DOI: | 10.1046/j.1365-2818.1999.00622.x | ISSN: | 0022-2720 |
Aparece en las colecciones: | (INCAR) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 59,24 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
13
checked on 14-may-2024
Page view(s)
89
checked on 16-may-2024
Download(s)
37
checked on 16-may-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.