Título: | Templated mesoporous carbons for supercapacitor application |
Autor: | Fuertes Arias, Antonio Benito CSIC ORCID ; Lota, G.; Álvarez Centeno, Teresa CSIC ORCID ; Frackowiak, Elzbieta | Palabras clave: | Supercapacitor Charge/discharge Template carbon Mesopores |
Fecha de publicación: | may-2005 | Citación: | Electrochimica Acta 50(14): 2799-2805 (2005) | Resumen: | Mesoporous carbons prepared by an inverse replica technique have been used as electrodes for electrochemical capacitors. Such well-sized carbons were prepared from mesostructured SBA-16 silica materials that served as templates whereas polyfurfuryl alcohol was the carbon precursor. Two highly mesoporous carbons characterized by 3 and 8 nm average pore diameter were tested in various electrolytic solutions (acidic, alkaline and aprotic). It can be concluded that templated mesoporous carbons with tailored pore size distribution are very promising materials to be used as electrodes in supercapacitors. The design of their pore size allows suiting the dimensions of electrolyte ions and efficient charging of the electrical double layer is achieved especially at high current load. Definitively better capacitance performance has been found for carbon with 3 nm pores range, however, cycling performance depends not only on the pore size. | Versión del editor: | http://dx.doi.org/10.1016/j.electacta.2004.11.027 | URI: | http://hdl.handle.net/10261/100330 | DOI: | 10.1016/j.electacta.2004.11.027 | ISSN: | 0013-4686 |
Aparece en las colecciones: | (INCAR) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
Templated_Centeno.pdf | 262,35 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
413
checked on 28-abr-2024
WEB OF SCIENCETM
Citations
377
checked on 29-feb-2024
Page view(s)
356
checked on 04-may-2024
Download(s)
614
checked on 04-may-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.