Título: | High thermoelectric performance in Bi2-xPbxBa2Co2Oy promoted by directional growth and annealing |
Autor: | Madre, M. A. CSIC ORCID; Costa, F. M.; Ferreira, N. M.; Rasekh, Sh.; Torres, M. A. CSIC ORCID ; Diez, J. C. CSIC ORCID; Amaral, Vitor S.; Amaral, J.S.; Sotelo, Andres CSIC ORCID | Palabras clave: | Grain growth Ceramics Doping Electrical properties Thermopower |
Fecha de publicación: | 2016 | Editor: | Elsevier | Citación: | Journal of the European Ceramic Society 36(1): 67-74 (2016) | Resumen: | Bi2-xPbxBa2Co2Oy (x=0.0, 0.2, 0.4, and 0.6) misfit compounds were grown by the laser floating zone technique. Microstructural analysis has shown the formation of thermoelectric grains together with high amount of secondary phases. Thermoelectric grains orientation is increased until 0.4Pb, while further substitution drastically destroys the preferential grain orientation. Electrical resistivity is very low compared with the values obtained in sintered materials, spectacularly increasing power factor. Moreover, the performance of these materials was further improved subjecting the as-grown samples to a postannealing step due to the rise of thermoelectric phase content. These microstructural modifications led to a high decrease of electrical resistivity, improving power factor in around a factor two at room temperature, compared with the as-grown samples. Moreover, the low thermal conductivity of the textured annealed samples leads to a maximum estimated ZT value of 0.53 for the 0.2 Pb-doped samples, much higher than the reported in literature. | Versión del editor: | http://doi.org/10.1016/j.jeurceramsoc.2015.09.034 | URI: | http://hdl.handle.net/10261/148418 | DOI: | 10.1016/j.jeurceramsoc.2015.09.034 | Identificadores: | doi: 10.1016/j.jeurceramsoc.2015.09.034 e-issn: 1873-619X issn: 0955-2219 |
Aparece en las colecciones: | (ICMA) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
growthannealing.pdf | 1,29 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
25
checked on 11-abr-2024
WEB OF SCIENCETM
Citations
23
checked on 24-feb-2024
Page view(s)
262
checked on 28-abr-2024
Download(s)
280
checked on 28-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.