Título

Magnetocaloric effect of Co62Nb6Zr2B 30 amorphous alloys obtained by mechanical alloying or rapid quenching

Autor Moreno, L.M.; Blázquez, J. S.; Ipus, J.J.; Borrego, J.M.; Franco, V. ; Conde Amiano, Alejandro
Fecha de publicación 2014
EditorAmerican Institute of Physics
Citación Journal of Applied Physics 115 (2014)
ResumenAmorphous samples of nominal composition Co62Nb 6Zr2B30 have been prepared using mechanical alloying (MA) and rapid quenching (RQ) techniques. Differences appear in Curie temperature and the phases developed after crystallization. Refrigerant capacity is enhanced 20% in the MA-sample with respect to that of RQ-sample. Neglecting the demagnetizing factor of powder samples significantly affects the exponent n characterizing the field dependence of the maximum magnetic entropy change. © 2014 AIP Publishing LLC.
URI http://hdl.handle.net/10261/98274
DOI10.1063/1.4857595
Identificadoresdoi: 10.1063/1.4857595
issn: 0021-8979
Aparece en las colecciones: (ICMS) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
JAPs.pdf535,36 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.