Título

Strain rate and loading modes in DMTA experiments on ethylene/propylene block copolymers

AutorRico, A.; Outón, P. R.; Salazar, A.; Benavente, Rosario ; Rodríguez, J.
Fecha de publicación2014
EditorKluwer Academic Publishers
CitaciónMechanics of Time-Dependent Materials 18: 407- 422 (2014)
ResumenA broad experimental programme using Dynamical-Mechanical Thermal Analysis (DMTA) was carried out on ethylene/propylene block copolymers (EPBC). The samples were subjected to frequency scans to evaluate the dependence of stored modulus on frequency. Tests were conducted on similar samples using different loading modes such as single cantilever, dual cantilever and tension configurations. If the stored modulus is plotted versus the test frequency, a different trend corresponding to each loading mode is obtained. Similar conclusions can be drawn regarding the glass transition temperature. In this work, strain rate, instead of frequency, is used to compare results provided by different loading modes. If the strain rate is used as the reference variable, a unique trend is observed despite the loading modes used to perform the experiment. © 2014 Springer Science+Business Media Dordrecht.
URIhttp://hdl.handle.net/10261/98171
DOI10.1007/s11043-014-9234-8
Identificadoresdoi: 10.1007/s11043-014-9234-8
issn: 1385-2000
e-issn: 1573-2738
Aparece en las colecciones: (ICTP) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.