Improved green strength of ceramics through aqueous gelcasting

AutorSantacruz, Isabel; Baudín de la Lastra, Carmen; Moreno Botella, Rodrigo María; Nieto, María Isabel
Palabras clavePolysaccharides
Compacts
Gelation
Agarose
Alumina
Fecha de publicación2004
EditorJohn Wiley & Sons
CitaciónAdvanced Engineering Materials 6: 672-676+611 (2004)
ResumenAqueous gelcasting of alumina is optimised by preparing concentrated agarose solutions under overpressure conditions. The better dissolution reduces the viscosity and improves the microstructural control leading to green densities higher than 60% of TD. The enhancement of the green strength is not accompanied by a significant increase of the plastic behaviour during fracture for agarose contents < 1 wt.%. Sintered densities > 99% of theoretical are obtained.
URIhttp://hdl.handle.net/10261/97575
DOI10.1002/adem.200400053
Identificadoresdoi: 10.1002/adem.200400053
issn: 1438-1656
Aparece en las colecciones: (ICV) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.