Effect of the chemistry and structure of the native oxide surface film on the corrosion properties of commercial AZ31 and AZ61 alloys

Autor Feliu Jr., S.; Maffiotte, C.; Samaniego, Alejandro; Galván Sierra, Juan Carlos; Barranco, Violeta
Palabras clave Magnesium alloys
Native oxide film
Chemistry and structure
Corrosion properties
XPS
Fecha de publicación 2011
EditorElsevier
Citación Applied Surface Science 267(20): 8558-8568 (2011)
ResumenThe purpose of this study has been to advance in knowledge of the chemical composition, structure and thickness of the thin native oxide film formed spontaneously in contact with the laboratory atmosphere on the surface of freshly polished commercial AZ31 and AZ61 alloys with a view to furthering the understanding of protection mechanisms. For comparative purposes, and to more fully describe the behaviour of the native oxide film, the external oxide films formed as a result of the manufacturing process (as-received condition) have been characterised. The technique applied in this research to study the thin oxide films (thickness of just a few nanometres) present on the surface of the alloys has basically been XPS (X-ray photoelectron spectroscopy) in combination with ion sputtering. Corrosion properties of the alloys were studied in 0.6 M NaCl by measuring charge transfer resistance values, which are deduced from EIS (electrochemical impedance spectroscopy) measurements after 1 h of exposure. Alloy AZ61 generally showed better corrosion resistance than AZ31, and the freshly polished alloys showed better corrosion resistance than the alloys in as-received condition. This is attributed to a combination of (1) higher thickness of the native oxide film on the AZ61 alloy and (2) greater uniformity of the oxide film in the polished condition. The formation of an additional oxide layer composed by a mixture of spinel (MgAl2O4) and MgO seems to diminish the protective properties of the passive layer on the surface of the alloys in as-received condition
Versión del editorhttp://dx.doi.org/10.1016/j.apsusc.2011.05.014
URI http://hdl.handle.net/10261/96220
DOI10.1016/j.apsusc.2011.05.014
ISSN0169-4332
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
chemistryass.pdf1,21 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.