Título

Synthesis and characterization of lead-free 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramic

AutorCoondoo, Indrani; Panwar, Neeraj; Amorín, Harvey; Algueró, Miguel ; Kholkin, A. L.
Fecha de publicación2013
EditorAmerican Institute of Physics
CitaciónJournal of Applied Physics 113(21): 214107 (2013)
ResumenPolycrystalline sample of lead-free 0.5Ba(Zr0.2Ti 0.8)O3-0.5(Ba0.7Ca0.3)TiO 3 ceramic has been synthesized by solid state reaction method. Single-phase perovskite structure with rhombohedral symmetry was confirmed by x-ray diffraction. Temperature dependent dielectric permittivity studies demonstrated frequency independent behavior, indicating that the studied sample was not a typical relaxor ferroelectric. A polymorphic phase transition between rhombohedral and tetragonal phase was noticed near room temperature followed by a tetragonal to cubic transition with 97 °C as the temperature of maximum permittivity. The macroscopic values of d33 and d31 were ∼350 pC/N and -141 pm/V, whereas the electromechanical coupling factors kp and kt were 44.5% and 41.6%, respectively. Bulk P-E hysteresis loop was obtained with saturation polarization 11 μC/cm 2 and coercive field ∼4 kV/cm. Distinct polarization contrast with a complex mosaic-like domain structure was observed in the out-of-plane mode of piezoresponse force microscopy. The domain width and the correlation length were estimated to be nearly 2 μm and 827 nm, respectively. Local hysteresis loop with apparent coercive voltage, Vc = 15.8 V, was observed. © 2013 AIP Publishing LLC.
Versión del editorhttp://dx.doi.org/10.1063/1.4808338
URIhttp://hdl.handle.net/10261/95550
DOI10.1063/1.4808338
Identificadoresdoi: 10.1063/1.4808338
issn: 0021-8979
e-issn: 1089-7550
Aparece en las colecciones: (ICMM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
characterization of lead-free.pdf3,56 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.