Long-term high temperature oxidation of CrAl(Y)N coatings in steam atmosphere

AutorMato, S.; Brizuela, Marta; Escobar Galindo, R.; Sánchez López, Juan Carlos
Palabras claveOxidation
High temperature corrosion
Weight loss
EPMA
Steel
Sputtered films
Fecha de publicación2014
EditorElsevier
CitaciónCorrosion Science 80: 453-460 (2014)
ResumenThe oxidation resistance of CrAl(Y)N coatings deposited by reactive magnetron sputtering on P92 steel substrates was tested at 650. °C in 100% steam atmosphere up to 2000. h of oxidation. Mass gain measurements and characterisation of coatings and scales after oxidation show the enhanced oxidation resistance provided by the coatings with respect to that of the substrate. The dominant influence of the film microstructure developed due to the presence of an adhesion interlayer of CrN at the coating/substrate interface over Y additions is evidenced. The best performance is achieved by a CrAlN dense coating of around 6. μm without adhesion interlayer. © 2013 Elsevier Ltd.
URIhttp://hdl.handle.net/10261/94702
DOI10.1016/j.corsci.2013.11.066
Identificadoresdoi: 10.1016/j.corsci.2013.11.066
issn: 0010-938X
e-issn: 1879-0496
Aparece en las colecciones: (ICMS) Artículos
(ICMM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.