Long range order and vacancy properties in Al-rich Fe3Al and Fe3Al(Cr) alloys

Autor Kim, S. M.; Morris, David G.
Palabras clave Fe3Al and Fe3Al(Cr) alloys
Interatomic bond energies
TEM
X-ray diffraction
Fecha de publicación 1998
EditorElsevier
Citación Acta Materialia 46: 2587-2602 (1998)
ResumenNeutron powder diffraction measurements have been carried out in situ from room temperature to about 100°C in Fe28Al (28 at.% Al), Fe32.5Al (32.5 at.% Al) and Fe28Al15Cr (28 at.% Al, 5 at.% Cr) alloys. X-ray diffraction and TEM studies provided supporting information. The data were analysed to obtain information about the temperature dependence of the DO3 and B2 long range order parameters, the location of the Cr atoms and their effect on the ordering energies, and on the vacancy formation and migration properties in Fe28Al and Fe32.5Al alloys. The location of the ternary alloying addition in DO3 and B2 ordered Al-rich Fe3Al is shown to be consistent with considerations of interatomic bond energies.
URI http://hdl.handle.net/10261/88048
DOI10.1016/S1359-6454(97)00464-3
Identificadoresdoi: 10.1016/S1359-6454(97)00464-3
issn: 1359-6454
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.