Effect of sintering temperature on the corrosion and wear behavior of protective SiO2-based sol-gel coatings

Autor Gallardo, J.; Durán, Alicia; García, Ignacio; Celis, J. P.; Arenas, M. A.; Conde, A.
Palabras clave Corrosion
Wear
Sol-gel coatings
Fecha de publicación 2003
EditorSpringer
Citación Journal of Sol-Gel Science and Technology 27: 175-183 (2003)
ResumenSol-gel hybrid organic-inorganic and inorganic SiO2-based protective coatings with and without added 3 μm glass particles were developed and tested for their corrosion and wear behavior of an stainless steel substrate (AISI316L). The corrosion resistance greatly increases by incorporating glass particles in the sols. The incorporation of particles in the coatings allows the synthesis of thicker crack-free coatings. On the other hand, the corrosion resistance increases for coatings with a higher organic content obtained at lower sintering temperature. These coatings are also highly stable in saline aqueous solutions. However, the wear resistance is badly affected by the hybrid character of the SiO2 matrix. The optimum coating process in terms of corrosion and wear resistance, appears to be a hybrid system with a dense SiO2 network achieved at intermediate sintering temperatures.
URI http://hdl.handle.net/10261/87988
DOI10.1023/A:1023702701850
Identificadoresdoi: 10.1023/A:1023702701850
issn: 0928-0707
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.