Enhanced reactivity and related optical changes of Ag nanoparticles on amorphous Al2O3 supports

Autor Peláez, Ramón J. ; Castelo, A; Afonso, Carmen N. ; Borrás, Ana ; Espinós, J.P. ; Riedel, S.; Leiderer, P.; Boneberg, J.
Fecha de publicación 2013
EditorInstitute of Physics Publishing
Citación Nanotechnology 24: 365702 (2013)
ResumenPairs of samples containing Ag nanoparticles (NPs) of different dimensions have been produced under the same conditions but on different substrates, namely standard glass slides and a thin layer of amorphous aluminum oxide (a-Al 2O3) on-glass. Upon storage in ambient conditions (air and room temperature) the color of samples changed and a blue-shift and damping of the surface plasmon resonance was observed. The changes are weaker for the samples on-glass and tend to saturate after 12 months. In contrast, the changes for the samples on a-Al2O3 appear to be still progressing after 25 months. While x-ray photoelectron spectroscopy shows a slight sulfurization and negligible oxidation of the Ag for the on-glass samples upon 25 months aging, it shows that Ag is strongly oxidized for the on a-Al 2O3 samples and sulfurization is negligible. Both optical and chemical results are consistent with the production of a shell at the expense of a reduction of the metal core dimensions, the latter being responsible for the blue-shift and related to the small (<10 nm initial diameter) of the NPs. The enhanced reactivity of the Ag NPs on the a-Al 2O3 supports goes along with specific morphological changes of the Ag NPs and the observation of nitrogen. © 2013 IOP Publishing Ltd.
URI http://hdl.handle.net/10261/87540
DOI10.1088/0957-4484/24/36/365702
Identificadoresdoi: 10.1088/0957-4484/24/36/365702
issn: 0957-4484
Aparece en las colecciones: (CFMAC-IO) Artículos
(ICMS) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.