Corrosion behaviour of amorphous Fe-Cr-Ni-(Si,P) alloys

AuthorsLópez, María Francisca ; Escudero Rincón, María Lorenza; Vida, E.; Pierna, A. R.
KeywordsAmorphous
XPS
AES
Corrosion
EIS
Issue Date1997
PublisherElsevier
CitationElectrochimica Acta 42(4): 659-665 (1997)
AbstractThe passive layers formed spontaneously via air contact on the surface of amorphous Fe62 Cr10 Ni8 X20 (X = Si,P) alloys were studied by X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES). The results for Fe62 Cr10 Ni8 Si20 showed the formation of a protective film, mainly consisting of oxidized chromium, that greatly enhanced the corrosion resistance of this alloy, whereas in Fe62 Cr10 Ni8 P20 the film was less corrosion resistant. To evaluate the influence of the passive layer composition on the corrosion resistance, standard electrochemical measurements on both alloys in 0.01 M HCl solution were performed. The study reveals that the best corrosion behaviour is given by the Si containing amorphous alloy confirming XPS and AES results. Copyright © 1996 Elsevier Science Ltd.
Publisher version (URL)http://doi.org/10.1016/S0013-4686(96)00211-3
URIhttp://hdl.handle.net/10261/82682
DOI10.1016/S0013-4686(96)00211-3
Identifiersissn: 0013-4686
Appears in Collections:(CENIM) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.