Title

Evaluation of mechanical properties and biological response of an alumina-forming Ni-free ferritic alloy

AuthorsGonzález-Carrasco, José Luis; Ciapetti, G.; Montealegre, M. A.; Pagani, S.; Chao, Jesús; Baldini, N.
Issue Date2005
PublisherElsevier
CitationBiomaterials 26: 3861-3871 (2005)
AbstractPM 2000 is a Ni-free oxide dispersion strengthened Fe-20Cr-5Al alloy able to develop a fine, dense and tightly adherent α-alumina scale during high-temperature oxidation. Despite the high temperature involved during thermal oxidation (1100°C), microstructural changes in the candidate material, a hot rolled product, hardly occurs. Consequently, the good mechanical properties of the as-received material are not significantly affected. Moreover, due to the high compressive residual stresses at the alumina scale, an increase in the fatigue limit from 500 to 530 MPa is observed. Such stresses also account for the high capability of the coating/metal system to withstand more than 1% tensile deformation without cracking. The biocompatibility of the alloy was assessed in comparison to commercial alumina. Saos-2 osteoblast-like cells were either challenged with PM 2000 particles, or seeded onto PM 2000 (with and without scale) solid samples. Viability, growth, and ALP release from cells were assessed after 3 or 7 days, while mineralization was checked at 18 days. This study has demonstrated that PM 2000 with and without scale are capable of supporting in vitro growth and function of osteoblast-like cells over a period of 18 days. Results from this study suggest that the resulting alumina/alloy system combines the good mechanical properties of the alloy with the superior biocompatibility of the α-alumina, for which there is very good clinical experience. © 2004 Elsevier Ltd. All rights reserved.
URIhttp://hdl.handle.net/10261/76775
DOI10.1016/j.biomaterials.2004.09.058
Identifiersdoi: 10.1016/j.biomaterials.2004.09.058
issn: 0142-9612
Appears in Collections:(CENIM) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.