Título: | Anticorrosion behavior of conversion coatings obtained from unbuffered cerium salts solutions on AA6061-T6 |
Autor: | Kiyota, S.; Valdez, B.; Stoytcheva, M.; Zlatev, R.; Bastidas Rull, José María | Fecha de publicación: | 2011 | Editor: | Elsevier | Citación: | Journal of Rare Earths 29: 961- 968 (2011) | Resumen: | The anticorrosive properties of cerium based conversion coatings deposited on AA6061-T6 alloy by immersion in unbuffered cerium chloride and cerium nitrate solutions in the presence of hydrogen peroxide were investigated and characterized by potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) in 0.5 mol/L NaCl aqueous solution. The microstructure and chemical composition of the protective films were examined by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). It was found that the best corrosion protection was afforded by the samples treated during 600 s in cerium chloride solution at pH values ∼5.5-4, showing higher amounts of cerium and polarization resistance values greater than 10 Ω m2. Moreover, an ennoblement of the corrosion potential and decreasing of the cathodic and anodic currents were obtained compared with the cerium nitrate solutions application. This behavior was attributed to the influence of the deposition parameters such as type of the salt anion, i.e., chelating effect and chaotropic characteristics, pH fluctuations in the conversion solution and deposition time. © 2011 The Chinese Society of Rare Earths. | URI: | http://hdl.handle.net/10261/76431 | DOI: | 10.1016/S1002-0721(10)60579-0 | Identificadores: | doi: 10.1016/S1002-0721(10)60579-0 issn: 1002-0721 |
Aparece en las colecciones: | (CENIM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
accesoRestringido.pdf | 15,38 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
28
checked on 15-abr-2024
WEB OF SCIENCETM
Citations
24
checked on 27-feb-2024
Page view(s)
293
checked on 18-abr-2024
Download(s)
122
checked on 18-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.