Title

The influence of chlorides, sulphates and nitrates at the coating-steel interface on underfilm corrosion

AuthorsMorcillo, Manuel; Rodríguez, F. J.; Bastidas Rull, José María
Issue Date1997
PublisherElsevier
CitationProgress in Organic Coatings 31: 245-253 (1997)
AbstractThe influence of water-soluble salts at the coating-steel interface on underfilm corrosion was studied. Vinyl and polyurethane varnishes were applied on mild steel contaminated with eight water-soluble chloride, sulphate and nitrate salts with Na+, NH+ 4 and Ca2+ as cations. The coated samples were exposed to condensed humidity for 100, 300 and 600 h. Rusting and blistering were visually evaluated. The underfilm corrosion rate was determined using a gravimetric technique. The study was completed by water and oxygen permeability tests on free coating films and by conductivity tests in aqueous electrolyte solutions. The corrosion stimulating salts exert an important effect on underfilm steel corrosion. Water permeability governs the coating adhesion and oxygen permeability controls the underfilm corrosion. The effect of the cations on underfilm corrosion seems to be masked by the effect of the anions. © 1997 Elsevier Science S.A.
URIhttp://hdl.handle.net/10261/76376
DOI10.1016/S0300-9440(97)00083-0
Identifiersdoi: 10.1016/S0300-9440(97)00083-0
issn: 0300-9440
Appears in Collections:(CENIM) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.