Title

Magnetic properties of epitaxial discontinuous Fe/MgO multilayers

AuthorsGarcía-García, A.; Pardo, J. A.; Magen, Cesar; Teresa, José María de; Morellón, Luis; Algarabel, Pedro A. ; Ibarra, M. Ricardo
Issue Date2012
PublisherAmerican Scientific Publishers
CitationJournal of Nanoscience and Nanotechnology 12(9): 7505-7509 (2012)
AbstractWe report magnetic, dynamic and transport properties of discontinuous metal-insulator multilayers Fe/MgO grown on amorphous Corning® glass and single-crystalline MgO (001) substrates. The films of structure Substrate/MgO (3 nm)/[Fe (0.6 nm)/MgO (3.0 nm)]×10 were prepared in ultra-high vacuum conditions using Pulsed Laser Deposition. It was shown that conditions of epitaxial growth are favorable for MgO substrates. As a result a substantial increase of tunneling magnetoresistance caused by spin-filtering effect was observed and reasonably theoretically explained. The value of TMR ̃ 9.2% at room temperature in 18 kOe magnetic field is three times higher comparing to that for the samples grown on Corning® glass substrates. Copyright © 2012 American Scientific Publishers All rights reserved.
URIhttp://hdl.handle.net/10261/73769
DOI10.1166/jnn.2012.6548
Identifiersdoi: 10.1166/jnn.2012.6548
issn: 1533-4880
e-issn: 1533-4899
Appears in Collections:(ICMA) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.