Optimization of the microstructure for improving superplastic forming in magnesium alloys

AuthorsValle, Jorge del; Peñalba, F.; Ruano, Oscar Antonio
KeywordsMagnesium alloys
Sheet forming
Severe plastic deformation; Grain size refinement
Superplasticity
Issue Date2007
PublisherElsevier
CitationMaterials Science and Engineering - A 467 (1-2) : 165-171 (2007)
AbstractThe deformation mechanisms and the thermal stability of AZ31 alloy, processed by various routes, have been investigated. Superplastic deformations could be achieved at flow stresses lower than 10 MPa at 375 °C and 10−4 s−1 in the AZ31 alloy with a grain size of 17 μm. The thermal stability of several magnesium alloys have been compared. It has been found that the forming temperature must be below but close to a limit temperature, which is a function of the grain size to obtain microstructural stability. Moreover, in the case of ultrafine grained magnesium alloys the stresses required for superplastic forming increase continuously reaching prohibitive levels because a fast decrease in the limit temperature occurs as the grain size is refined. To perform superplastic blow forming in magnesium alloys it is proposed the use of fine, but not ultrafine, grain sizes with the condition of deformation being controlled by grain boundary sliding.
Publisher version (URL)http://dx.doi.org/10.1016/j.msea.2007.02.088
URIhttp://hdl.handle.net/10261/58790
DOI10.1016/j.msea.2007.02.088
ISSN0921-5093
Appears in Collections:(CENIM) Artículos
Files in This Item:
There are no files associated with this item.
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.