Título: | Superplastic behavior of a kappa carbide material (Fe3AlCx) |
Autor: | Kim, W. J.; Ruano, Oscar Antonio CSIC ORCID; Wolfenstine, J.; Frommeyer, G.; Sherby, O. D. | Palabras clave: | Creep Superplastic iron carbide Compression |
Fecha de publicación: | 1997 | Editor: | Materials Research Society | Citación: | Journal of Materials Research 12(9) : 2317-2324 (1997) | Resumen: | Fine-grained kappa carbide (Fe3AlCx) materials, containing 12.5 and 14% Al, and 3.5% C, were prepared by powder processing and hipping procedures. The creep behavior of the kappa materials was shown to be identical to that observed in superplastic iron carbide, and was shown to follow a grain boundary–diffusioncontrolled grain boundary sliding relation. The tensile fracture strains in kappa, however, were shown to be considerably less than in iron carbide with a maximum elongation of 92% noted. This difference is attributed to either a low stress intensity factor or to contamination of the powder surface in the kappa material. The compression creep strength, at a given strain rate, was shown to be about two times higher than the tension creep strength. | Versión del editor: | http://dx.doi.org/10.1557/JMR.1997.0307 | URI: | http://hdl.handle.net/10261/58266 | DOI: | 10.1557/JMR.1997.0307 | ISSN: | 0884-2914 |
Aparece en las colecciones: | (CENIM) Artículos |
Mostrar el registro completo
CORE Recommender
SCOPUSTM
Citations
8
checked on 19-mar-2024
WEB OF SCIENCETM
Citations
7
checked on 28-feb-2024
Page view(s)
487
checked on 27-mar-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.