Title

Study of the stability of the molten zone and the stresses induced during the growth of Al2O3–Y3Al5O12 eutectic composite by the laser floating zone technique

AuthorsSola, D.; Ester, Francisco Javier; Oliete, Patricia B.; Peña, J. I.
KeywordsAl2O3
YAG
Thermal shock resistance
Defects
Eutectic
Issue DateJun-2011
PublisherElsevier
CitationJournal of the European Ceramic Society 31(7): 1211-1218 (2011)
AbstractA series of analytical calculations is used to study both the effect of the thermal gradients and the stability of the molten zone in the laser floating zone growth of Al2O3–Y3Al5O12 eutectic composite. The thermal gradients in the solidification interface have been calculated and the axial gradient compared with the experimental one of 4.5 × 105 K/m. For these calculations the coefficients of heat transfer from the molten zone to the ambient at the solid-melt interface have been previously obtained. The thermal stresses generated by the high thermal gradients can induce crack formation during the cooling depending on the rod diameter. The theory predicts that it is possible to grow rods free of cracks up to R = 1.7 mm, at low rates (10 mm/h) in close agreement with the experimental critical radius of 1.6 mm.The dependence of the zone length on the input laser power used to carry out the growth is shown. The study of the floating zone profile allows determining the maximum stable zone length, verifying the stability criterion established by some authors.
Description8 páginas, 7 figuras.
Publisher version (URL)http://dx.doi.org/10.1016/j.jeurceramsoc.2010.08.022
URIhttp://hdl.handle.net/10261/55735
DOI10.1016/j.jeurceramsoc.2010.08.022
ISSN0955-2219
Appears in Collections:(ICMA) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.