Reactividad y aptitud a la cocción de crudos de cemento con elevados contenidos en manganeso Reactivity and burnability of cement raw materials Witt) iiigli manganese content

Abstract

[EN]It has been verified that high manganese content in raw mixes causes alters the mineralogical composition of clinkers. New phases like 2 CaO.Mn02 and Ca2AIMnO¿ are developed and C^A formation can be inhibited. Manganese is a flux similar to iron in the traditional raw mixes. The presence of manganese will modify the expressions of the lime saturation factor (LSF), silica modulus (Ms) and aluminium modulus (Mf). This has as consequence an increase of the proportion of intersticial phase in the obtained clinkers.

[ES] Se ha comprobado que contenidos elevados de manganeso en el crudo provoca una modificación significativa en la composición mineralógica del clinker. Se desarrollan las fases no tradicionales 2 CaO.Mn02 y Ca2AIMnOQ, y se puede llegar, incluso, a inhibir la formación de alumínate tricálcico. El manganeso tiene un comportamiento fundente muy similar al jugado por el hierro en los crudos tradicionales, por lo que la incorporación de óxidos de manganeso al crudo produce una alteración significativa en los módulos tradicionales (LSF, Ms y Mf). Esto tiene como consecuencia inmediata un gran incremento en la proporción de fase instersticial en los clínkeres producidos