Study by DTA/TG of the formation of calcium aluminate obtained from an aluminium hazardous waste

AutorLópez-Delgado, Aurora ; López Gómez, Félix Antonio ; González-Delgado, L.; López-Andrés, Sol; Alguacil, Francisco José
Palabras claveAluminium waste
Calcium aluminate
TG/DTA
Fecha de publicación2010
EditorSpringer
CitaciónJournal of Thermal Analysis and Calorimetry 99 (3) : 999-1004 (2010)
ResumenA Spanish hazardous waste from tertiary aluminium industry was used as a raw material for the synthesis of calcium aluminate. An amorphous precursor was obtained by a hydrothermal method at different values of pH. The transformation of the precursor in a crystalline aluminate was followed by TG/DTA up to 1300 C. At temperatures between 719 and 744 C, the precursors evolve towards the formation of C12A7 which becomes CA at circa 1016 C. Mass spectrometry coupled to thermal analyser allowed the identification of the decomposition products
Versión del editorhttp://dx.doi.org/10.1007/s10973-009-0597-z
URIhttp://hdl.handle.net/10261/47277
DOI10.1007/s10973-009-0597-z
ISSN1388-6150
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Journal of Thermal Analysis and Calorimetry 99 (3) 999-1004 (2010).pdf1,17 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.