Título: | Estudio dieléctrico de cerámicas de textura y microestructura controladas con composiciones (SrBi2Nb2O9)(1-x)(Bi3TiNbO9)x |
Otros títulos: | Dielectric properties of ceramics of composition (SrBi2Nb2O9)(1-x)(Bi3TiNbO9)x with controled texture and microstructure | Autor: | Moure Arroyo, Alberto CSIC ORCID ; Jiménez, Ricardo CSIC ORCID; Alemany, C.; Pardo, Lorena CSIC ORCID | Palabras clave: | Ferroeléctricos Cerámicas SrBi2Nb2O9 Bi3TiNbO9 Permitividad dieléctrica Ferroelectrics Dielectric Permittivity |
Fecha de publicación: | ene-2002 | Editor: | Sociedad Española de Cerámica y Vidrio | Citación: | Boletín de la Sociedad Española de Cerámica y Vidrio 41(1): 40-44 (2002) | Resumen: | [ES] Se han preparado cerámicas de la solución sólida (SrBi2Nb2O9)1-x(Bi3TiNbO9)x con x = 0.35, 0.65 y 1.00 y estructura tipo
Aurivillius obtenidas por sinterización natural y por prensado en caliente. Se parte de precursores amorfos obtenidos por
activación mecanoquímica de una mezcla estequiométrica de óxidos y carbonatos, lo que permite utilizar temperaturas
moderadas de procesado. Estos materiales son interesantes por su posible uso como piezoeléctricos de alta temperatura. La
caracterización dieléctrica permite establecer a qué temperatura se encuentra la transición ferro-paraeléctrica que limita la
temperatura de uso del material y como afectan las propiedades eléctricas, especialmente la conductividad d. c., a la polarizabilidad
de las cerámicas, así como su relación con su microestructura y textura. En este trabajo se ha realizado el estudio
dieléctrico de estos materiales en el intervalo de frecuencias de 100 Hz a 5 MHz y en el rango de temperaturas desde 200 ºC
hasta temperaturas por encima de la de la transición ferro-paraeléctrica de cada composición (>900 ºC para Bi3TiNbO9). [EN] Ceramics of composition (SrBi2Nb2O9)1-x(Bi3TiNbO9)x with x = 0.35, 0.65 and 1.00 and Aurivillius type structure have been prepared by natural sintering and hot pressing. Amorphous precursors were obtained by mechanochemical activation of stoichiometric mixtures of oxides and carbonates, which allows using moderate processing temperatures. These materials are interesting for their use as high temperature piezoelectrics. Dielectric characterisation allows to know the temperature at what takes place the ferro-paraelectric transition, which limits the working temperature of the material. It also gives information on how the electric properties, especially the d. c. conductivity, affect the polarizability of the ceramics. The properties relation with the microstructure and the texture is studied. In this work, dielectric studies of these materials have been made, in the frequency interval from 100 Hz to 5 MHz and in the temperature range from 200 ºC up to the ferroparaelectric transition temperatures (>900 ºC for Bi3TiNbO9). |
Versión del editor: | http://boletines.secv.es/es/index.php?id=42&vol=41 | URI: | http://hdl.handle.net/10261/4694 | ISSN: | 0366-3175 |
Aparece en las colecciones: | (ICMM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
microestructura.pdf | 344,64 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
Page view(s)
401
checked on 23-abr-2024
Download(s)
245
checked on 23-abr-2024
Google ScholarTM
Check
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.