Title

Hydrogen embrittlement of high-strength steel submitted to slow strain rate testing studied by nuclear resonance reaction analysis and neutron diffraction

AuthorsCastellote, M.; Fullea, J. ; Viedma, P. G. de; Andrade, C.; Alonso, C.; Llorente, I.; Turrillas, Xabier M.
KeywordsStress corrosion cracking
Slow strain rate testing
High-strength steel
Hydrogen embrittlement
Nuclear reaction analysis (NRRA)
Neutron diffraction
Steels
Issue Date2007
PublisherElsevier
CitationNuclear Instruments and Methods in Physics Research - Section B; Vol. 259; nº 2; págs. 975-983; (2007)
AbstractEmbrittlement of high-strength steel is known to be caused by hydrogen penetration into the network of the metal. However, the penetration mechanism of hydrogen into the steel is still under discussion, as it is not so easy to detect and measure the hydrogen in steels. In this paper, relatively large commercial cold drawn pearlitic steel wires have been submitted to stress corrosion cracking under different environments. After these tests, Nuclear Resonance Reaction Analysis, NRRA, has been used to detect the presence of the hydrogen and its quantity, which has confirmed the presence of H in the case of brittle fracture. In addition, once the presence of hydrogen has been confirmed, the penetration of the hydrogen into the unit cell of the ferrite has been deduced from the analysis of the steels by neutron diffraction, from the shift of the d-spacing after the experiments. The application of NRRA and Neutron Diffraction techniques have been shown as very promising techniques to study the mechanisms of the embrittlement of the steel to the hydrogen present in the metallic lattice.
Publisher version (URL)http://www.sciencedirect.com/science/article/pii/S0168583X07007082
URIhttp://hdl.handle.net/10261/46816
ISSN0168-583X
Appears in Collections:(CISDEM) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.