Título : Dependencia térmica del proceso de inversión de la imanación en microhilos magnéticos biestables
Otros títulos: Magnetization reversal process in bistable microwires and its temperature dependence en microhilos magnéticos biestables
Autor : Vázquez Valero, Manuela; Zhukov, A. P.; García, K. L.; Pirota, K. R. ; Varga, Rastislav; Martínez, J. L.
Palabras clave : Microhilos magnéticos amorfos
Inversión de la imanación
Dependencia con la temperatura
Biestabilidad magnética
Magnetic amorphous microwires
Magnetization reversal
Temperature dependence
Magnetic bistability
Fecha de publicación : mar-2004
Editor: Sociedad Española de Cerámica y Vidrio
Citación : Boletín de la Sociedad Española de Cerámica y Vidrio 43(2): 532-535 (2004)
Resumen: [ES] En este trabajo se resumen los más recientes resultados alcanzados relativos al comportamiento magnético de microhilos amorfos ricos en Fe cubiertos de capa aislante en función de la temperatura de medida (en el rango de 5 a 300 K). Estos microhilos, debido a su elevada magnetostricción, presentan comportamiento magnético biestable cuando su longitud supera un valor crítico determinado por la intensidad de la anisotropía magnética axial. Esta anisotropía depende en particular del espesor de la cubierta protectora de Pyrex, de modo que al reducir la temperatura se inducen fuertes tensiones mecánicas (hasta 400 MPa) como consecuencia de la diferencia de valor del coeficiente de expansión térmica con el núcleo metálico. Se comprueba asímismo que el modo de sujección del microhilo al portamuestras puede generar fuertes tensiones de compresión y dar lugar a la desaparición de comportamiento biestable.
[EN] The temperature dependence of the magnetic behaviour of Fe-based glass-coated amorphous microwires with positive magnetostriction has been studied in the temperature range from 5 to 300 K. For long enough microwires, hysteresis loops are squared shaped in the whole temperature range denoting the existence of a large domain with axial easy axis. For short microwires, magnetic bistability is partially lost near room temperature but may be recovered at low temperature. This is interpreted considering the influence of the shape anisotropy: in short wires the demagnetizing field may become large enough to destroy the single domain structure. The influence of coating is also considered by studying microwires with different coating thickness. Transverse magnetoelastic anisotropy up to around 400 MPa can be induced at low temperature as a consequence of the difference in thermal expansion coefficients between metallic nucleus and insulating coat. Additional changes in the low-temperature loops have been identified to be a consequence of the way how the microwires are fixed to the sample´s holder. Under particular circumstances transverse anisotropy induced at low temperature may destroy the bistable behavior.
Versión del editor: http://boletines.secv.es/es/index.php?id=18&vol=43
URI : http://hdl.handle.net/10261/4552
ISSN: 0366-3175
Aparece en las colecciones: (ICMM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
microhilos.pdf756,18 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.