Título : Síntesis y caracterización de composites de TPOS reforzados con nanotubos de carbono
Otros títulos: Synthesis and Characterization of Composites based on TPOs Reinforced with Carbon Nanotubes
Autor : Biagiotti, J.; Valentini, L.; Kenny, José María ; López Manchado, M. A.; Arroyo Ramos, Víctor Miguel
Palabras clave : Nanotubos de carbono
TPOs
Espectroscopía Raman
Fecha de publicación : mar-2004
Editor: Sociedad Española de Cerámica y Vidrio
Citación : Boletín de la Sociedad Española de Cerámica y Vidrio 43(2): 527-531 (2004)
Resumen: [ES] En el presente estudio se han preparado nanocomposites de elastómeros termoplásticos basados en mezclas de polipropileno (PP) y terpolímeros de etileno-propileno dieno (EPDM) reforzados con nanotubos de carbono. En concreto, se ha analizado el efecto de la incorporación de los nanotubos sobre las propiedades físicas y térmicas del material. Los resultados indican que los nanotubos actúan como nucleantes, acelerando notablemente la cristalización del PP en mezclas PP-EPDM. Es importante destacar que este efecto no es lineal con el porcentaje de nanotubos en el composite, observándose una saturación a altos contenidos de nanotubos. Se ha observado que la máxima nucleación se obtiene a concentraciones de 0.5% de nanotubos en el composite. El análisis mecanodinámico muestra resultados similares, observándose un aumento del módulo de almacenamiento a bajos contenidos de nanotubos, disminuyendo considerablemente a concentraciones de nanotubos superiores al 0.5%. Por su parte, la espectroscopía Raman y microscopía electrónica de barrido permitieron determinar que estos cambios en las propiedades se deben a cambios estructurales en el composite.
[EN] Polymer composites based on thermoplastic elastomer and single-walled carbon nanotubes have been investigated. In particular, the effect of the incorporation of SWNTs on physical and thermal properties of the material are described. The results indicate that the SWNT act as nucleant agent, sensibly accelerating the PP crystallization in PP-EPDM blends. It is of interest to note that this effect is not linearly dependent on the SWNTs’ content, showing a saturation of the nucleant effect at high nanotube concentrations. The maximum nucleant effect was observed at low nanotubes concentration (0.5%). Similar results were obtained by dynamic mechanical analysis, with an increase of the storage modulus by incorporating of low nanotubes contents. However, a further increase in the SWNTs content dramatically decreases the storage modulus. Raman spectroscopy and scanning electron microscopy were successfully applied to demonstrate that changes in the properties of the composite films, can be explained in terms of the structural variations in the composite.
Versión del editor: http://boletines.secv.es/es/index.php?id=18&vol=43
URI : http://hdl.handle.net/10261/4550
ISSN: 0366-3175
Aparece en las colecciones: (ICTP) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
tpos.pdf379,81 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.