Título : Optimización de espinelas LiCoyMn2-yO4 para electrodos positivos de baterías recargables de ion-litio mediante ajuste del dopado y de la temperatura de síntesis
Otros títulos: Optimization of LiCoYMn2-YO4 spinel positive electrodes for li-ion batteries by adjusting dopand and synthesis temperature
Autor : Amarilla, José Manuel ; Rojas, Rosa M. ; Pérez Revenga, M. L.; Larrazaga, M. G.; Mandal, S.; Rojo, J. M.
Palabras clave : Espinelas LiCoyMn2-yO4
LiCoyMn2-yO4
Material de cátodo
Bateria de litio
LiCoyMn2-yO4 spinels
Cathode material
Lithium battery
Fecha de publicación : mar-2004
Editor: Sociedad Española de Cerámica y Vidrio
Citación : Boletín de la Sociedad Española de Cerámica y Vidrio 43(2): 127-131 (2004)
Resumen: [ES] Se han sintetizado espinelas LiCoyMn2‑yO4 (0<y≤0.33) con óptimas propiedades electroquímicas en la región de 4V mediante un procedimiento original basado en la reacción a 750º C entre las espinelas Co3y/2Mn3-3y/2O4 obtenidas a temperatura ambiente y LiOH.H2O. Los materiales obtenidos se han caracterizado por difracción de rayos-X, y la disminución del parámetro de red observada ha sido asociada con el aumento del porcentaje de dopante. Se han estudiado las propiedades electroquímicas mediante ciclaje galvanostático en una celda de litio. Se ha analizado la influencia del dopado en la capacidad, el potencial redox y la ciclabilidad de las espinelas sintetizadas. El compuesto LiCo0.11Mn1.89O4 es el material que presenta las mejores propiedades electroquímicas, con una capacidad inicial de Q = 121.7 mA h g-1 y una reversibilidad por ciclo del 99.86%.
[EN] The synthesis of LiCoyMn2‑yO4 (0<y≤0.33) spinels with optimised electrochemical performances in the 4V region has been carried out. They have been obtained by an original procedure designed by us, based on the reaction at 750ºC between the corresponding amounts of Co3y/2Mn3- 3y/2O4 spinels precursors obtained at room temperature, and LiOH.H2O. The samples have been characterized by X-ray powder diffraction, and the diminution observed in the lattice parameter has been associated with the increase of the dopant content. Electrochemical properties of the spinels have been analysed by galvanostatic cycling in a lithium cell. The influence of the dopant content on the capacity, the redox potential, and the cyclability of the spinels have also been studied. The LiCo0.11Mn1.89O4 material is the one showing better properties, with a starting capacity of Q = 121.7 mA h g‑1 and 99.86% reversibility by cycle.
Versión del editor: http://boletines.secv.es/es/index.php?id=18&vol=43
URI : http://hdl.handle.net/10261/4453
ISSN: 0366-3175
Aparece en las colecciones: (ICMM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
electrodos.pdf931,05 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.