Título : Ultra-high–strength Bainitic Steels
Autor : García Mateo, Carlos; García Caballero, Francisca
Palabras clave : Carbon content
Bainite
Mechanical properties
Plate thickness
Dislocation density
Fecha de publicación : 2005
Editor: Iron and Steel Institute of Japan
Citación : ISIJ International, Vol. 45 (2005), No. 11, pp. 1736–1740
http://db1.wdc-jp.com/isij/abst/200511/is451736.html
Resumen: Novel bainitic microstructures, consisting of slender ferrite plates (tens of nm) in a matrix of retained austenite, have reported maximum yield strength of 1.4 GPa, ultimate tensile strength of 2.2 GPa, 30% ductility and respectable levels of fracture toughness (∼51 MPa m0.5). The unusual combination of properties is attributed to the fine bainitic plates and the presence of retained austenite in the microstructure.
URI : http://hdl.handle.net/10261/3186
ISSN: 0915-1559
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ISIJ_2005_45_1736.pdf655,58 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.