Título : Acceleration of Low-temperature Bainite
Autor : García Mateo, Carlos; García Caballero, Francisca; Bhadeshia, H. K. D. H.
Palabras clave : Bainite
Retained austenite
Phase transformations
Kinetics
Fecha de publicación : 2003
Editor: Iron and Steel Institute of Japan
Citación : ISIJ International, Vol. 43 (2003), No. 11, pp. 1821–1825
http://db1.wdc-jp.com/isij/abst/200311/is431821.html
Resumen: Recent work has shown that bainitic ferrite plates produced by transformation at low temperatures can be as thin as 20 nm with a hardness in excess of 650 HV. However, it may take several days in order to achieve the required degree of transformation at low temperatures. In this work we report methods for accelerating the rate of reaction without compromising strength.
URI : http://hdl.handle.net/10261/3181
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ISIJ_2003_43_1821.pdf176,05 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.