Título : Development of Hard Bainite
Autor : García Mateo, Carlos; García Caballero, Francisca; Bhadeshia, H. K. D. H.
Palabras clave : Phase transformations
Bainite
Steel
Hardness
Fecha de publicación : 2003
Editor: Iron and Steel Institute of Japan
Citación : ISIJ International, 43 (8): 1238–1243 (2003)
Resumen: It is demonstrated that in a high-carbon steel where carbide precipitation is suppressed, bainite can be obtained by isothermal transformation at temperatures as low as 200°C. The time taken for nucleation at this temperature can be many days, but the transformation results in the growth of extremely thin platelets of bainite, so thin that the hardness of the resulting steel can be greater than 600 HV.
Descripción : 6 páginas, 8 figuras, 2 tablas.
Versión del editor: http://www.journalarchive.jst.go.jp/jnlpdf.php?cdjournal=isijinternational1989&cdvol=43&noissue=8&startpage=1238〈=en&from=jnltoc
URI : http://hdl.handle.net/10261/3180
ISSN: 0915-1559
E-ISSN: 1347-5460
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ISIJ_2003_43_1238.pdf1,37 MBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.