Título: | Formation of YBa2Cu3O7–δ superconducting films by electrodeposition |
Autor: | Martín-González, Marisol CSIC ORCID ; García-Jaca, Javier; Morán, Emilio; Alario-Franco, Miquel Á. | Fecha de publicación: | 1999 | Editor: | Royal Society of Chemistry (UK) | Citación: | Journal of Materials Chemistry 9(6): 1293-1298 (1999) | Resumen: | Superconducting thick films of Y-Ba-Cu-O have been prepared via an electrodeposition procedure of the constituent metals on metallic substrates (Cu, Ag) followed by an oxidative thermal treatment. The films were electrodeposited at a constant potential of –3.5 V (vs. Ag/AgCl) from a single electrolyte bath, which contains the nitrates of the cations in dimethyl sulfoxide. The initial state of the precursor film and the formation process of the final superconducting film have been followed by IR spectroscopy, thermogravimetric analysis, X-ray diffraction and scanning electron microscopy. In the precursor film, yttrium and copper are present as metals while barium forms a carbonate. Dimethyl sulfoxide (DMSO) is not inert under the experimental conditions and oxidises to the sulfone. The superconducting transition temperature (Tc) of the final film was ≈92 K and the critical current density (Jc) values were ≈9 500 A cm–2 at 77 K and zero field, the highest so far obtained by electrodeposition. | Descripción: | 6 páginas, 10 figuras, 3 tablas. | Versión del editor: | http://dx.doi.org/10.1039/A809172B | URI: | http://hdl.handle.net/10261/28744 | DOI: | 10.1039/A809172B | ISSN: | 0959-9428 |
Aparece en las colecciones: | (IMN-CNM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
1999-01-01.pdf | 652,8 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
WEB OF SCIENCETM
Citations
4
checked on 16-feb-2024
Page view(s)
333
checked on 19-abr-2024
Download(s)
285
checked on 19-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.