Título: | Control of structural and magnetic properties of polycrystalline Co2FeGe films via deposition and annealing temperatures |
Autor: | Vovk, Andrii; Bunyaev, Sergey A.; Štrichovanec, Pavel; Vovk, Nikolay R.; Postolnyi, Bogdan; Apolinario, Arlete; Pardo, J. A. CSIC ORCID; Algarabel, Pedro A. CSIC ORCID; Kakazei, Gleb N.; Araujo, João Pedro | Palabras clave: | Thin films Ferromagnetic resonance Heusler alloys Magnetostatic properties |
Fecha de publicación: | 2021 | Editor: | Multidisciplinary Digital Publishing Institute | Citación: | Nanomaterials 11(5): 1229 (2021) | Resumen: | Thin polycrystalline Co2FeGe films with composition close to stoichiometry have been fabricated using magnetron co-sputtering technique. Effects of substrate temperature (TS) and post-deposition annealing (Ta) on structure, static and dynamic magnetic properties were systematically studied. It is shown that elevated TS (Ta) promote formation of ordered L21 crystal structure. Variation of TS (Ta) allow modification of magnetic properties in a broad range. Saturation magnetization ~920 emu/cm3 and low magnetization damping parameter α ~ 0.004 were achieved for TS = 573 K. This in combination with soft ferromagnetic properties (coercivity below 6 Oe) makes the films attractive candidates for spin-transfer torque and magnonic devices. | Descripción: | This article belongs to the Special Issue Magnetic and Magnetoelectric Nanomaterials: Synthesis, Characterization and Applications. | Versión del editor: | https://doi.org/10.3390/nano11051229 | URI: | http://hdl.handle.net/10261/265581 | DOI: | https://doi.org/10.3390/nano11051229 | E-ISSN: | 2079-4991 |
Aparece en las colecciones: | (INMA) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
controltemp.pdf | 7,88 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
Page view(s)
25
checked on 27-mar-2024
Download(s)
45
checked on 27-mar-2024
Google ScholarTM
Check
Altmetric
Altmetric
Este item está licenciado bajo una Licencia Creative Commons