Título: | Confinement in extruded nanocomposites based on pcl and mesoporous silicas: Effect of pore sizes and their influence in ultimate mechanical response |
Autor: | Díez-Rodríguez, Tamara M. CSIC ORCID; Blázquez-Blázquez, Enrique CSIC ORCID ; Antunes, N. L. C,; Ribeiro, M. D. R.; Pérez, Enrique; Cerrada, María L. CSIC ORCID | Palabras clave: | Mesoporous silica MCM-41 and SBA-15 PCL nanocomposites Synchrotron SAXS measurements Crystallites Rigidity modulus |
Fecha de publicación: | 2021 | Editor: | Multidisciplinary Digital Publishing Institute | Citación: | Journal of Composites Science 5: 321 (2021) | Resumen: | In this study, nanocomposites based on polycaprolactone (PCL) and two types of mesoporous silicas, MCM-41 and SBA-15, were attained by melt extrusion. The effect of the silica incorporated within the PCL matrix was observed, firstly, in the morphological characteristics and degradation behavior of the resultant composites. DSC experiments provided information on the existence of confinement in the PCL¿SBA-15 materials through the appearance of an additional small endotherm, located at about 25¿50¿C, and attributed to the melting of constrained crystallites. Displacement to a slightly lower temperature of this endothermic event was observed in the first heating run of PCL¿MCM-41 composites, attributed to the inferior pore size in the MCM-41 particles. Thus, this indicates variations in the inclusion of PCL chains within these two mesostructures with different pore sizes. Real-time variable-temperature small-angle X-ray scattering (SAXS) experiments with synchrotron radiation were crucial to confirm the presence of PCL within MCM-41 and SBA-15 pores. Accurate information was also deduced from these measurements regarding the influence of these two mesoporous MCM-41 and SBA-15 silicas on PCL long spacing. The differences found in these morphological and structural features were responsible for the ultimate mechanical response exhibited by the two sets of PCL nanocomposites, with a considerably higher increase of mechanical parameters in the SBA-15 family. | Versión del editor: | http://dx.doi.org/10.3390/jcs5120321 | URI: | http://hdl.handle.net/10261/258131 | DOI: | 10.3390/jcs5120321 | Identificadores: | doi: 10.3390/jcs5120321 issn: 2504-477X |
Aparece en las colecciones: | (ICTP) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
860632.pdf | 4,81 MB | Unknown | Visualizar/Abrir |
CORE Recommender
Page view(s)
24
checked on 16-abr-2024
Download(s)
43
checked on 16-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.