Título

Modificación superficial de aleaciones de base aluminio (anodizadas y no anodizadas) mediante recubrimientos de sílice

Otros títulosSuperficial modification of aluminium-base alloys (anodising and non-anodising) by silica coatings
AutorGarcía Heras, Manuel ; González Mena, E.; Villegas Broncano, María Ángeles
Palabras claveRecubrimientos
Modificación superficial
Reflectancia
Durabilidad
Sol-gel
Coatings
Superficial modification
Reflectance
Durability
Fecha de publicación30-abr-2004
EditorConsejo Superior de Investigaciones Científicas (España)
CitaciónRevista de Metalurgia 40(2): 127-131 (2004)
Resumen[ES] Se han depositado recubrimientos transparentes e incoloros de sílice sobre sustratos anodizados y no anodizados de aleaciones de base aluminio (serie 6063). Los recubrimientos se prepararon por sol-gel (inmersión-extracción) a partir de un alcóxido de silicio y de una mezcla de alcóxido y alquilalcóxido de silicio. La optimización de las fonnulaciones se basó en medidas de viscosidad, densidad, tensión superficial y ángulo de contacto. La densificación se llevó a cabo a 60 y 120 °C. La atenuación de la reflectancia luminosa de las muestras recubiertas se analizó por espectroscopia UV-VIS-IRP. Los resultados indicaron que se alcanza casi un 10 % de atenuación. Los ensayos de durabilidad y resistencia a la degradación del sistema metal/recubrimiento se realizaron por inmersión en disoluciones acuosas, aplicando medidas de impedancia electroquímica y del potencial de corrosión del sustrato metálico, para tiempos variables.
[EN] Transparent and colourless silica coatings were deposited on anodising and non-anodising substrates of aluminium-base alloys (series 6063). Coatings were prepared by soLgel (dipping method) from a silica alkoxide and a mixture of both silica alkoxide and silica alkylalkoxide. Preparations were optimised from viscosity, density, surface tension, and contact angle measurements. Densification was carried out at 60 and 120 °C. Reflectance attenuation of coated samples was analysed by UV-VIS-NIR spectroscopy. The results indicated that -10 % of attenuation is reached. Durability and resistance against degradation tests of the metal/coating system were undertaken by immersion into aqueous solutions. Electrochemical impedance measurements and potential corrosion of the metallic substrate for variable times were performed.
Descripción5 páginas, 2 figuras, 2 tablas.
Versión del editorhttp://dx.doi.org/10.3989/revmetalm.2004.v40.i2.253
URIhttp://hdl.handle.net/10261/21214
DOI10.3989/revmetalm.2004.v40.i2.253
ISSN0034-8570 (Print)
1988-4222 (Online)
Aparece en las colecciones: (CENIM) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
253-262-1-PB.pdf276,7 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.