Título: | Lixiviación ácida de concentrados de scheelita |
Otros títulos: | Acid leaching of scheelite concentrates | Autor: | Navarro, Patricio; Vargas, C.; Alguacil, Francisco José CSIC ORCID | Palabras clave: | Lixiviación Ácido Concentrado Wolframio Scheelita Leaching Acid Concentrate Tungsten Scheelite |
Fecha de publicación: | 30-abr-2005 | Editor: | Consejo Superior de Investigaciones Científicas (España) | Citación: | Revista de Metalurgia 41(2): 107-110 (2005) | Resumen: | [ES] Se estudió la lixiviación acida, en medio clorhídrico, de un concentrado de wolframio
(scheelita, CaW04). De lo anterior, se obtuvo un sólido insoluble (H2WO4), que se trató
con una solución alcalina de hidróxido de sodio, lográndose la completa solubilización del
wolframio como ion wolframato (WO4 ). La fracción transformada de wolframio aumenta
con la temperatura, como también con una granulometría más fina. Se logró una disolución
máxima de 88,5 % (400 g/1 HCl, 363 K y 20 j^lm de tamaño de partícula) para 3 h de
proceso, disolución que se interpretó a través del modelo de núcleo recesivo con formación
de capa de producto sólido para todo el rango de variación de los parámetros en estudio. El
valor de energía de activación encontrado fue de 28,0 k]/mol. [EN] The acid leaching in hydrochloric media of a tungsten concentrate (scheelite, CaWO^) was studied. Of the above-mentioned, an insoluble solid (H2WO4) was obtained which were treated with an alkaline solution of sodium hydroxide, achieving the complete solubilization of the tungsten as wolframate ion (WO4 ). The transformed fraction of tungsten increases with the temperature, as well as with a finer grain. A maximum dissolution of 88.5 % (400 g/1 HCl, 363 K and 20 jLim of particle size) was achieved for a 3 h process, of the disolution process was interpreted by the recessive core model with formation of a layer of solid product for the whole range of variation of the parameters in study. The activation energy value was found to be 28.0 kj/mol. |
Descripción: | 4 páginas, 6 figuras. | Versión del editor: | http://dx.doi.org/10.3989/revmetalm.2005.v41.i2.193 | URI: | http://hdl.handle.net/10261/21194 | DOI: | 10.3989/revmetalm.2005.v41.i2.193 | ISSN: | 0034-8570 | E-ISSN: | 1988-4222 |
Aparece en las colecciones: | (CENIM) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
193-199-1-PB.pdf | 159,09 kB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
5
checked on 20-abr-2024
Page view(s)
443
checked on 24-abr-2024
Download(s)
666
checked on 24-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.