High-Temperature Tensile Strength of Er2O3-Doped ZrO2 Single Crystals

AutorPastor, José Y.; Llorca-Martínez, F. Javier; Poza, Pedro; Quispe, José J.; Arellano López, A. R. de; Martínez-Fernández, Julián; Sayir, Ali; Orera, V. M.
Palabras claveFracture
Mechanisms in tension
Fecha de publicación13-abr-2006
EditorAmerican Ceramic Society
John Wiley & Sons
CitaciónJournal of the American Ceramic Society 89 (7): 2140-2146 (2006)
ResumenThe deformation and fracture mechanisms in tension were studied in single-crystal Er2O3-doped ZrO2 monofilaments processed by the laser-heated floating zone method. Tensile tests were carried out between 25° and 1400°C at different loading rates and the dominant deformation and fracture mechanisms were determined from the shape of the stress–strain curves, the morphology of the fracture surfaces, and the evidence provided by monofilaments deformed at high temperature and broken at ambient temperature. The tensile strength presented a minimum at 600°–800°C and it was controlled by the slow growth of a crack from the surface. This mechanism was also dominant in some monofilaments tested at 1000°C and above, while others showed extensive plastic deformation before fracture at these temperatures. The strength of plastically deformed monofilaments was significantly higher than those which failed by slow crack growth due to the marked strain hardening capacity of this material.
Versión del editorhttp://dx.doi.org/10.1111/j.1551-2916.2006.00995.x
Aparece en las colecciones: (ICMA) Artículos
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Mostrar el registro completo

Artículos relacionados:

NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.