Properties of doped ex and in situ MgB2 multifilament superconductors

AutorKováč, P.; Hušek, I.; Melišek, T.; Martínez, Elena; Dhalle, M.
Fecha de publicación13-sep-2006
EditorInstitute of Physics Publishing
CitaciónSuperconductor Sciencie and Technology 19: 1076-1082 (2006)
ResumenFour-filament ex and in situ MgB2 wires were prepared with the rectangular wire-in-tube (RWIT) technique. Based on experience with single-core wires, 10 wt% of W was added to the ex situ and 10 wt% of SiC to the in situ powders, which were packed into Fe and Nb/AgMg tubes, respectively, and two-axially rolled into composite conductors. The ex and in situ conductors are compared in terms of field-dependent transport critical current density, effects of filament size reduction and twisting, mechanical behaviour and thermal stability.
Descripción7 pages, 11 figures, 1 table.
Versión del editorhttp://dx.doi.org/10.1088/0953-2048/19/10/016
URIhttp://hdl.handle.net/10261/19688
DOI10.1088/0953-2048/19/10/016
ISSN1742-6588
Aparece en las colecciones: (ICMA) Artículos
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.