Carbon coating and reaction on magnesia-alumina spinel

AutorMazzoni, A. D.; Sainz Trigo, M. Antonia; Aglietti, E. F.; Caballero Cuesta, Amador
Palabras claveSpinel
Stability
Fecha de publicación2007
EditorElsevier
CitaciónMaterials Chemistry and Physics 101 (2007) 211–216
ResumenThe reactions that took place in the spinel and in the carbon–spinel interface at high temperatures (1250–1800 ◦C) under low oxygen partial pressure (PO2 ≤ 10−16 MPa) are described in detail. Scanning electron microscopy equipped with microanalysis by energy dispersion (SEM-EDS) and X-ray diffraction lattice parameter have been used to determine the extent of solid solubility of Al2O3 in MgAl2O4. The Al2O3/MgO spinel ratio at different temperatures in air and packed with carbon were also determined. The behavior of spinel under these reducing conditions was discussed.
Versión del editorhttp://dx.doi.org/10.1016/j.matchemphys.2005.04.060
URIhttp://hdl.handle.net/10261/19194
DOI10.1016/j.matchemphys.2005.04.060
Aparece en las colecciones: (ICV) Artículos
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.