Tape casting of Y-TZP with low binder content

AutorGurauskis, Jonás; Baudín de la Lastra, Carmen; Sánchez Herencia, Antonio Javier
Palabras claveSuspensions
Tape casting
Fecha de publicación2007
EditorElsevier
CitaciónCeramics International 33 (2007) 1099–1103
ResumenThe rheology of Y-TZP slurries with a low content of an acrylic/styrene binder is studied. The optimum amount of dispersant was found to be 0.3 wt.% for the starting slurry. After a 5 wt.% of binder addition the dispersant amount needed to achieve a minimum viscosity increases to 0.5 wt.%. Tapes obtained from slurries with a solid content of 45 vol.% shows the higher green density of 51 th.%. Higher solid contents do not yield to better green densities due to the high viscosity.
Versión del editordoi:10.1016/j.ceramint.2006.03.014
URIhttp://hdl.handle.net/10261/18588
DOI10.1016/j.ceramint.2006.03.014
Aparece en las colecciones: (ICV) Artículos
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.