Rapid densification by using Bi2O3 as an aid for sinterin of gadolinia-doped ceria ceramics

AutorGil, Vanesa; Tartaj, Jesús; Moure Jiménez, Carlos; Durán Botia, Pedro
Palabras claveSintering
Grain growth
Fecha de publicación2007
EditorElsevier
CitaciónCeramics International 33 (2007) 471–475
ResumenDensification process and microstructure development in Bi2O3-doped gadolinia ceria (GDC) submicrometer powders have been studied by the constant heating rate (CHR) method in air and by SEM observations. Densification of GDC was strongly enhanced by adding small amounts of Bi2O3, and samples of GDC containing 1 wt% Bi2O3 sintered at 1200–1400 8C for 2 to 4 h were near theoretically dense bodies (98–99.8% of theoretical), i.e., about 250–300 8C lower than that for undoped-GDC ceramics. A transient liquid phase-assisting mechanism was assumed to be the main cause for such an improvement. The grain size of GDC ceramics was hardly affected by the Bi2O3 additions during sintering. A total electrical conductivity as high as 4 S m 1 at 700 8C for the doped-GDC samples sintered at 1400 8C, was measured.
Versión del editordoi::10.1016/j.ceramint.2005.10.012
URIhttp://hdl.handle.net/10261/18431
DOI10.1016/j.ceramint.2005.10.012
Aparece en las colecciones: (ICV) Artículos
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.