Indium-tin oxide thin films deposited at room temperature on glass and PET substrates: Optical and electrical properties variation with the H2-Ar sputtering gas mixture

AuthorsÁlvarez-Fraga, L.; Jiménez-Villacorta, Félix ; Sánchez-Marcos, J. ; Andrés, Alicia de ; Prieto, C.
KeywordsIndium tin oxide (ITO)
Polyethylene terephthalate (PET)
Magnetron sputtering
Issue Date30-Jul-2015
PublisherElsevier
CitationApplied Surface Science 344: 217-222 (2015)
AbstractThe optical and electrical properties of indium tin oxide (ITO) films deposited at room temperature on glass and polyethylene terephthalate (PET) substrates were investigated. A clear evolution of optical transparency and sheet resistance with the content of H2 in the gas mixture of H2 and Ar during magnetron sputtering deposition is observed. An optimized performance of the transparent conductive properties ITO films on PET was achieved for samples prepared using H2/(Ar + H2) ratio in the range of 0.3–0.6%. Moreover, flexible ITO-PET samples show a better transparent conductive figure of merit, ΦTC = T10/RS, than their glass counterparts. These results provide valuable insight into the room temperature fabrication and development of transparent conductive ITO-based flexible devices.
Publisher version (URL)https://doi.org/10.1016/j.apsusc.2015.03.096
URIhttp://hdl.handle.net/10261/182869
Identifiersdoi: 10.1016/j.apsusc.2015.03.096
issn: 0169-4332
Appears in Collections:(ICMM) Artículos
Files in This Item:
File Description SizeFormat 
accesoRestringido.pdf15,38 kBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.