Oxidation treatments for SiC particles and its compatibility with glass

AutorVillegas, Marina; Sierra, T.; Lucas, F.; Fernández Lozano, José Francisco; Caballero Cuesta, Amador
Palabras claveOxidation
SiC
Fecha de publicación2007
EditorElsevier
CitaciónJournal of the European Ceramic Society 27 (2007) 861–865
ResumenDifferent thermal treatments were performed to produce a protective coating on the surface of SiC particles in order to allow their incorporation in a glass matrix. These oxidation treatments were carried out in air at different temperatures ranging from 800 ◦C to 1500 ◦C and different times at 1200 ◦C (10 min–48 h). The oxidation kinetics followed the Deal–Grove model and the thickness of the protective coating increased with temperature and SiC particle size. Protected SiC particles with different particle sizes were incorporated in a borosilicate glass.With small particles sizes foam glasses were obtained, whereas particles with higher grain size, i.e., higher coating thickness, were stable in the glass matrix and a smooth glass was obtained.
Versión del editorhttp://dx.doi.org/10.1016/j.jeurceramsoc.2006.04.041
URIhttp://hdl.handle.net/10261/17392
DOI10.1016/j.jeurceramsoc.2006.04.041
Aparece en las colecciones: (ICV) Artículos
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.