Título

Physical properties of biaxially oriented poly(ethyleneterephtalate) irradiated at different temperatures and doses with electron beam

AutorAdema, E.; Rubio Hernández-Sampelayo, A.; Báez, J. E.; Miranda, J.; Labrada-Delgado, G. J.; Marcos-Fernández, Ángel
Palabras clavePoly(ethylene terephtalate)
Tensile properties
Thermal properties
Electron beam irradiation
Fecha de publicación2017
EditorElsevier
CitaciónRadiation Physics and Chemistry 130: 5-11 (2017)
ResumenThe electron beam irradiation of a biaxially oriented PET film was carried out in air over a range of 50¿3000 kGy at different temperatures and a dose rate of 4.48 kGy min-1. The effects of the irradiation at temperatures above and below the glass transition temperature (Tg) on the thermal and mechanical properties were studied. Melting temperature decreased slightly and crystallization temperature and crystallinity increased significantly with the increase in dose, more at higher irradiation temperature, whereas Tg did not show any significant change with dose or temperature. Mechanical properties were adversely affected by irradiation. Stress and strain at break were strongly reduced, more at higher irradiation temperature, and Young's Modulus slightly increased with the increase in dose. The changes in properties were related to the chain scission produced by the electron beam irradiation leading to a decrease in molecular weight.
Versión del editorhttp://dx.doi.org/10.1016/j.radphyschem.2016.07.022
URIhttp://hdl.handle.net/10261/157398
DOI10.1016/j.radphyschem.2016.07.022
Identificadoresdoi: 10.1016/j.radphyschem.2016.07.022
issn: 0969-806X
Aparece en las colecciones: (ICTP) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.