Título

Sol-gel synthesis of the lithium-ion conducting perovskite La0.57Li0.3TiO3 effect of synthesis and thermal treatments on the structure and conducting properties

AutorWöhrle, T.; Gómez-Romero, P. ; Fries, T.; West, K.; Palacín, M. R.; Casañ Pastor, Nieves
Palabras claveLithium-ion conducting
Perovskite
La0.57Li0.3TiO3
Fecha de publicación17-sep-1996
EditorSpringer
CitaciónIonics 2 (5-6): 442-445 (1996)
ResumenThe lithium ionic conducting perovskite La0.57Li0.3TiO3 has been synthesised via a sol-gel method at a temperature of 700 °C. The crystallinity of the product can be greatly increased by further heat treatment at 1000 °C. In this paper the product of the sol-gel synthesis is compared with the product of conventional solid-state synthesis, and the influence of the synthesis method as well as of quenching on the crystal structure and ionic conductivity has been studied. AC-impedance measurements show two contributions to the ionic conductivity, which can be adscribed to intergranular and intragranular effects, respectively. A lower intergranular resistivity is observed for sol-gel samples, while quenching mainly affects the materials prepared by solid-state reaction. The crystal structure of the material prepared by the sol-gel method is identical to that of the material prepared by the solid state reaction, although the synthesis temperature is nearly 600 °C lower. A tetragonal superstructure is observed when either type of material is slowly cooled from 1300 °C. Quenching from the same temperature results in the suppression of that superstructure.
DescripciónPaper presented at the 3rd Euroconference on Solid State Ionics, Teulada, Sardinia, Italy, Sept. 15–22, 1996.
Versión del editorhttp://dx.doi.org/10.1007/BF02375824
URIhttp://hdl.handle.net/10261/15707
DOI10.1007/BF02375824
ISSN0947-7047 (Print)
1862-0760 (Online)
Aparece en las colecciones: (ICMAB) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
accesoRestringido.pdf15,38 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 



NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.