Modified Ti/MCM-41 catalysts for enantioselective epoxidation of styrene

AutorFadhli, Marwa; Khedher, Ilyes; Fraile, José M.
Palabras claveEnantioselective epoxidation
MCM-41
Titanium
Styrene oxide
Fecha de publicación2016
EditorElsevier
CitaciónJournal of Molecular Catalysis A: Chemical 420: 282-289 (2016)
ResumenTi sites grafted on MCM-41, pretreated at different temperatures, have been modified with chiral tartrates, leading to different species. Those solids are active catalyst for the epoxidation of styrene with tert-butyl hydroperoxide, although their efficiency is not optimal, mainly due to the subsequent epoxide rearrangement to phenyl acetaldehyde and further oxidation of it. Styrene oxide is obtained with moderate enantioselectivity, in the range of 55-62% e.e., and the best overall results correspond to the use of MCM-41 calcined at the lowest temperature (550 °C). These results are much better with regard to styrene oxide selectivity than those obtained in homogeneous phase under the same conditions, whereas enantioselectivity is similar. The heterogeneous catalysts are recoverable, but only partially due to a loss in activity, although enantioselectivity is kept at similar levels, demonstrating the stability of the supported Ti-tartrate species.
Versión del editorhttps://doi.org/10.1016/j.molcata.2016.05.001
URIhttp://hdl.handle.net/10261/155637
DOI10.1016/j.molcata.2016.05.001
Identificadoresdoi: 10.1016/j.molcata.2016.05.001
issn: 1381-1169
Aparece en las colecciones: (ISQCH) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
epoxidationstyrene.pdf452,91 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 

Artículos relacionados:


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.