Title

Wide-Range Magnetoelectric Response on Hybrid Polymer Composites Based on Filler Type and Content

AuthorsMartins, Pedro; Silva, Marco; Reis, Silvia; Pereira, Nelson; Amorín, Harvey; Lanceros-Méndez, Senentxu
Issue Date14-Feb-2017
PublisherMultidisciplinary Digital Publishing Institute
CitationPolymers 9 (2): 62 (2017)
AbstractIn order to obtain a wide-range magnetoelectric (ME) response on a ME nanocomposite that matches industry requirements, Tb0.3Dy0.7Fe1.92 (Terfenol-D)/CoFe<sub>2</sub>O<sub>4</sub>/P(VDF-TrFE) flexible films were produced by the solvent casting technique and their morphologic, piezoelectric, magnetic and magnetoelectric properties were investigated. The obtained composites revealed a high piezoelectric response (≈−18 pC·N<sup>−1</sup>) that is independent of the weight ratio between the fillers. In turn, the magnetic properties of the composites were influenced by the composite composition. It was found that the magnetization saturation values decreased with the increasing CoFe<sub>2</sub>O<sub>4</sub> content (from 18.5 to 13.3 emu·g<sup>−1</sup>) while the magnetization and coercive field values increased (from 3.7 to 5.5 emu·g<sup>−1</sup> and from 355.7 to 1225.2 Oe, respectively) with the increasing CoFe<sub>2</sub>O<sub>4</sub> content. Additionally, the films showed a wide-range dual-peak ME response at room temperature with the ME coefficient increasing with the weight content of Terfenol-D, from 18.6 to 42.3 mV·cm<sup>−1</sup>·Oe<sup>−1</sup>.
Publisher version (URL)http://doi.org/10.3390/polym9020062
URIhttp://hdl.handle.net/10261/149354
DOI10.3390/polym9020062
Identifiersdoi: 10.3390/polym9020062
Appears in Collections:(ICMM) Artículos
Files in This Item:
File Description SizeFormat 
polymers-09-00062.pdf1,39 MBAdobe PDFThumbnail
View/Open
Show full item record
Review this work
 

Related articles:


WARNING: Items in Digital.CSIC are protected by copyright, with all rights reserved, unless otherwise indicated.