Título

Improvement of thermoelectric properties in Ca3Co4O9 ceramics by Ba doping

AutorConstantinescu, G.; Rasekh, Sh.; Torres, M. A.; Madre, M. A.; Sotelo, A.; Diez, J. C.
Fecha de publicación2015
EditorSpringer
CitaciónJournal of Materials Science: Materials in Electronics 26(6): 3466-3473 (2015)
ResumenCa3−xBaxCo4O9 bulk polycrystalline thermoelectric ceramics with x = 0.00, 0.01, 0.03 and 0.05 have been prepared through a classical solid state method. Microstructural characterizations of sintered samples have shown that Ba has been incorporated into the Ca3Co4O9 and/or Ca3Co2O6 structures and that no Ba-based secondary phases have been produced. The apparent density values increase when the amount of barium is raised with respect to the undoped samples, reaching a maximum value of around 77 % of the Ca3Co4O9 theoretical density, for samples with the highest amount of barium. Electrical resistivity of doped samples decreases in the whole measured temperature range with respect to the undoped ones, while Seebeck coefficient remains practically unchanged. In conclusion, the improvement in resistivity leads to power factor values which are higher than the ones measured in undoped samples, fact which makes this bulk polycrystalline compound a promising candidate for high-temperature power generation applications in oxidative environments.
Versión del editorhttps://doi.org/10.1007/s10854-015-2856-z
URIhttp://hdl.handle.net/10261/147781
DOI10.1007/s10854-015-2856-z
Identificadoresdoi: 10.1007/s10854-015-2856-z
e-issn: 1573-482X
issn: 0957-4522
Aparece en las colecciones: (ICMA) Artículos
Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Badoping.pdf651,79 kBAdobe PDFVista previa
Visualizar/Abrir
Mostrar el registro completo
 


NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.