Título: | Effect of secondary annealing process on critical current density in highly textured Bi-2212 superconducting system |
Autor: | Aksan, M. A.; Madre, M. A. CSIC ORCID; Rasekh, Sh.; Constantinescu, G. CSIC ORCID; Torres, M. A. CSIC ORCID ; Diez, J. C. CSIC ORCID; Sotelo, Andres CSIC ORCID; Yakinci, M. E. | Fecha de publicación: | 2015 | Editor: | Springer Nature | Citación: | JOM 67(9): 2079-2086 (2015) | Resumen: | Bi-2212 samples prepared by a solid-state reaction technique have been grown from the melt using the laser floating zone method. After annealing the as-grown bars, the samples showed a good grain alignment and a high transport critical current density. Secondary annealing processes were performed on the annealed samples with the aim of producing Bi-2212 phase controlled decomposition. Hence, the Bi-2201 phase and the secondary phases, which act as effective pinning centers, were obtained with the secondary annealing process. After these thermal treatments, the transport critical current densities of samples significantly increased, when compared to the annealed ones. The maximum critical current density was achieved when the samples were subjected to secondary annealing at 680°C for 168 h with an improvement of ~80%, compared to the annealed ones. Moreover, it was found that magnetization of the secondarily annealed samples was also increased. The magnetic critical current densities in these secondary annealed samples were about 3 times higher than the values obtained for the annealed ones. These results clearly indicate that the secondary annealing processes lead to the formation of effective pinning centers in the bulk material. | Versión del editor: | https://doi.org/10.1007/s11837-015-1509-2 | URI: | http://hdl.handle.net/10261/147639 | DOI: | 10.1007/s11837-015-1509-2 | Identificadores: | doi: 10.1007/s11837-015-1509-2 issn: 1543-1851 |
Aparece en las colecciones: | (ICMA) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
147639ANNEALING.pdf | 1,02 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
SCOPUSTM
Citations
3
checked on 17-abr-2024
WEB OF SCIENCETM
Citations
3
checked on 28-feb-2024
Page view(s)
259
checked on 23-abr-2024
Download(s)
284
checked on 23-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.