Título: | Diferenciación cinética y morfológica de Ettringitas mediante Metakaolín, cementos Portland y el ensayo ASTM C 452-68. Parte I: diferenciación cinética. |
Otros títulos: | Kinetic and morphological differentiation of Ettringites in plain and blended Portland cements using Metakaolin and the ASTM C 452-68 test. Part I: kinetic differentiation. | Autor: | Talero Morales, Rafael CSIC | Palabras clave: | Eettringitas Metakaolín Cementos Portlánd Yeso Ettringites Metakaolin Portland cements Gypsum |
Fecha de publicación: | 1-dic-2008 | Editor: | Consejo Superior de Investigaciones Científicas (España) | Citación: | Materiales de Construcción 58 (292): 45-66 (2008) | Resumen: | [ES] En esta Parte I de la investigación, se han logrado verifi-
car mediante el ensayo ASTM C 452-68, los resultados
obtenidos en anteriores investigaciones realizadas con
DRX y SEM y el ensayo Le Chatelier-Ansttet. Para ello, a
10 cementos Portland –6 CPO y 4 CPRS– se les añadió
20%, 30% y 40% de metakaolín (MK). Tanto los 10 CP
como los 30 de sus mezclas con metakaolín (MK), se
ensayaron durante 2 años, mediante dicho método ASTM
C 452-68, y a sus probetas no sólo se les determinó su
incremento porcentual de longitud, ∆L(%), sino además,
el contenido de sulfatos de sus aguas de conservación.
Otras determinaciones complementarias fueron: análisis
químico de los materiales cementiceos utilizados y pro-
piedades específicas de algunos cementos ensayados.
Los resultados experimentales, ∆L(%) frente al tiempo,
han confirmado de nuevo que la velocidad de formación
de la ettringita de origen alúmina reactiva, Al2O3 r-, de las
puzolanas, tiene que ser considerablemente mayor que la
velocidad de formación de la ettringita de origen C3A de
los CP, lo que ha sido verificado por la evolución durante
todo el ensayo, del contenido de sulfatos de las aguas de
conservación de las probetas. Debido a ello, se ha pro-
puesto denominar a ambos tipos de ettringitas, ettringita
de rápida formación, ett-rf, y ettringita de lenta forma-
ción, ett-lf, respectivamente. [EN] In this first part of the study, the results obtained in prior research with XRD and SEM, as well as the Le Chatelier- Ansttet test were confirmed with the ASTM C 452-68 test. To this end, 20%, 30% and 40% metakaolin (MK) was added to ten Portland cements, six OPCs and four SRPCs. Both the ten plain PCs and the 30 metakaolin (MK) blends were tested for two years under ASTM C 452-68 specifications, determining not only the percentage increase in length, ΔL(%), of the specimens, but also the sulphate content in the curing water. Other parameters studied included: chemical analysis of the cementitious materials used and specific properties of some of the cements tested. The experimental results, ΔL(%) versus time, re-confirmed that the formation rate of ettringite from the reactive alumina, Al2O3 r-, present in the pozzolan must be substantially higher than the formation rate of ettringite from the C3A present in the PC. This was verified by the variation of the sulphate content in the specimen curing water throughout the test. In light of those findings, in this article these two types of ettringite are denominated rapid forming ettringite or ett-rf, and slow forming ettringite or ett-lf. |
Descripción: | 22 pages, 3 figures, 5 tables. | Versión del editor: | http://dx.doi.org/10.3989/mc.2008.30805 | URI: | http://hdl.handle.net/10261/14357 | DOI: | 10.3989/mc.2008.v58.i292.116 | ISSN: | 0465-2746 | E-ISSN: | 1988-3226 |
Aparece en las colecciones: | (IETCC) Artículos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
155.pdf | 3,29 MB | Adobe PDF | Visualizar/Abrir |
CORE Recommender
Page view(s)
309
checked on 22-abr-2024
Download(s)
203
checked on 22-abr-2024
Google ScholarTM
Check
Altmetric
Altmetric
NOTA: Los ítems de Digital.CSIC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.